T1 Evaluation of the corrosion behavior of AZ31Mg alloy used as sacrificial anode for cathodic protection of hot water tank storage containing chloride
A1 Souto, Ricardo Manuel
A1 Zidane, N.
A1 Ait Albrimi, Y.
A1 Ait Addi, A.
A1 Douch, J.
A1 Hamdani, M.
K1 Corrosion
K1 Cathodic protection
K1 Sacrificial anode
K1 Magnesium alloy AZ31
K1 Potentiodynamic polarization
K1 Electrochemical impedance spectroscopy
AB Corrosion resistance of AZ31 magnesium alloy was evaluated in aqueous chloride-containing solutions. Combined weight loss and electrochemical data indicate that corrosion rate of magnesium alloy increased for greater NaCl concentrations and higher temperatures. Corrosion is characterized by the formation of precipitates, that present the distinctive XRD patterns corresponding to crystalline phases of Mg(OH)2, accompanied by H2 evolution, these processes leading to pH increases in the solution. Retrieved samples show a film of corrosion products distributed around cracks on the bare metal surface, and the subsequent development of large pits that prevent the material from attaining passive protection.
YR 2018
FD 2018
LK http://riull.ull.es/xmlui/handle/915/18993
UL http://riull.ull.es/xmlui/handle/915/18993
LA en
DS Repositorio institucional de la Universidad de La Laguna
RD 14-nov-2024